Handbook of Comparative World Steel Standards Part 7 pot

Chapter 5 Steel Tubes and Pipes 227


Handbook of Comparative World Steel Standards
5.9 Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures

5.9.2A Chemical Composition of Austenitic Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures (Continued)

Weight, %, max, Unless Otherwise Specified
Standard
Designation
Grade, Class, Type,
Symbol or Name
Steel
Number
UNS
Number
C Mn Si P S Cr Ni Mo Others
ASTM A 213/A 213M-03a TP304H S30409 0.04-0.10 2.00 0.75 0.040 0.030 18.0-20.0 8.00-11.0
ASTM A 249/A 249M-03 TP304H S30409 0.04-0.10 2.00 1.00 0.045 0.030 18.0-20.0 8.0-11.0
ASTM A 312/A 312M-03 TP304H S30409 0.04-0.10 2.00 1.00 0.045 0.030 18.0-20.0 8.0-11.0
ASTM A 358/A 358M-01 304H S30409 0.04-0.10 2.00 0.75 0.045 0.030 18.0-20.0 8.0-10.5
ASTM A 376/A 376M-02a TP304H S30409 0.04-0.10 2.00 0.75 0.045 0.030 18.0-20.0 8.00-11.0
JIS G 3459:1997 SUS304HTP 0.04-0.10 2.00 0.75 0.040 0.030 18.00-20.00 8.00-11.00
JIS G 3463:1994 SUS304HTB 0.04-0.10 2.00 0.75 0.040 0.030 18.00-20.00 8.00-11.00
JIS G 3467:1988 SUS 304H TF 0.04-0.10 2.00 0.75 0.040 0.030 18.00-20.00 8.00-11.00
BS 3605-1:1991 AMD 2:1997 304S51 0.04-0.10 2.00 1.00 0.040 0.030 17.00-19.00 8.00-11.00
DIN 17459:1992 X 6 CrNi 18 11 1.4948 0.04-0.08 2.0 0.75 0.035 0.015 17.0-19.0 10.0-12.0
AFNOR NF A 49-214:1978 Z 6 CN 19-10 0.04-0.08 2.0 1.0 0.035 0.030 18-20 8-11
ISO 2604-II:1975 TS 48 0.04-0.09 2.00 0.75 0.045 0.030 17.00-20.00 8.00-12.00
ASTM A 249/A 249M-03 S30615 0.16-0.24 2.00 3.2-4.0 0.030 0.030 17.0-19.5 13.5-16.0

AFNOR NF A 49-217:1987 TU Z 1 CNS 18 15 0.015 2.00 3.50-4.50 0.030 0.020 16.50-18.50 13.80-16.00 0.50
ASTM A 213/A 213M-03a TP309S S30908 0.08 2.00 0.75 0.045 0.030 24.0-26.0 12.00-15.00 0.75
ASTM A 249/A 249M-03 TP309S S30908 0.08 2.00 1.00 0.045 0.030 22.0-24.0 12.0-15.0
ASTM A 312/A 312M-03 TP309S S30908 0.08 2.00 1.00 0.045 0.030 22.0-24.0 12.0-15.0 0.75
ASTM A 358/A 358M-01 309S S30908 0.08 2.00 0.75 0.045 0.030 22.0-24.0 12.0-15.0
JIS G 3459:1997 SUS309STP 0.08 2.00 1.00 0.040 0.030 22.00-24.00 12.00-15.00
JIS G 3463:1994 SUS309STB 0.08 2.00 1.00 0.040 0.030 22.00-24.00 12.00-15.00
JIS G 3468:1994 SUS309S 0.08 2.00 1.00 0.045 0.030 22.00-24.00 12.00-15.00
ASTM A 213/A 213M-03a TP309H S30909 0.04-0.10 2.00 0.75 0.045 0.030 22.00-24.00 12.00-15.00 0.75
ASTM A 249/A 249M-03 TP309H S30909 0.04-0.10 2.00 1.00 0.045 0.030 22.0-24.0 12.0-15.0
JIS G 3459:1997 SUS309TP 0.15 2.00 1.00 0.040 0.030 22.00-24.00 12.00-15.00
JIS G 3463:1994 SUS309TB 0.15 2.00 1.00 0.040 0.030 22.00-24.00 12.00-15.00
AFNOR NF A 49-244:1993 X15CrNi24-13 0.15 2.00 0.75 0.035 0.015 22.0-24.0 12.0-14.0
ASTM A 213/A 213M-03a TP310S S31008 0.08 2.00 0.75 0.045 0.030 24.00-26.00 19.00-22.00 0.75
ASTM A 249/A 249M-03 TP310S S31008 0.08 2.00 1.00 0.045 0.030 24.0-26.0 19.0-22.0
ASTM A 312/A 312M-03 TP310S S31008 0.08 2.00 1.00 0.045 0.030 24.0-26.0 19.0-22.0 0.75
ASTM A 358/A 358M-01 310S S31008 0.08 2.00 1.50 0.045 0.030 24.0-26.0 19.0-22.0
JIS G 3459:1997 SUS310STP 0.08 2.00 1.50 0.040 0.030 24.00-26.00 19.00-22.00
JIS G 3463:1994 SUS310STB 0.08 2.00 1.50 0.040 0.030 24.00-26.00 19.00-22.00
JIS G 3468:1994 SUS310S 0.08 2.00 1.50 0.045 0.030 24.00-26.00 19.00-22.00

Chapter 5 Steel Tubes and Pipes 228


Handbook of Comparative World Steel Standards
5.9 Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures

5.9.2A Chemical Composition of Austenitic Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures (Continued)

Weight, %, max, Unless Otherwise Specified

Standard
Designation
Grade, Class, Type,
Symbol or Name
Steel
Number
UNS
Number
C Mn Si P S Cr Ni Mo Others
ASTM A 213/A 213M-03a TP310H S31009 0.04-0.10 2.00 0.75 0.040 0.030 24.00-26.00 19.0-22.00
AFNOR NF A 49-244:1993 X1CrNi25-20 0.015 2.00 0.40 0.025 0.010 24.0-26.0 19.0-22.0 0.5
JIS G 3463:1994 SUS310TB 0.15 2.00 1.50 0.040 0.030 24.00-26.00 19.00-22.00
JIS G 3467:1988 SUS310TF 0.15 2.00 1.50 0.040 0.030 24.00-26.00 19.00-22.00
ISO 2604-II:1975 TS 68 0.15 2.00 0.75 0.045 0.030 24.00-26.00 19.00-22.00
ASTM A 249/A 249M-03 S31050 0.030 2.00 0.40 0.030 0.015 24.0-26.0 21.0-23.0 2.00-3.00 0.10-0.16
AFNOR NF A 49-217:1987 TU Z 1 CND 25 22 AZ 0.020 1.50-2.00 0.40 0.020 0.015 24.50-26.00 21.50-23.00 1.90-2.40 N 0.10-0.15
ASTM A 249/A 249M-03 S31254 0.020 1.00 0.80 0.030 0.010 19.5-20.5 17.5-18.5 6.0-6.5 N 0.18-0.25; Cu 0.50-1.00
ASTM A 688/A 688M-03 S31254 0.020 1.00 0.80 0.030 0.010 19.5-20.5 17.5-18.5 6.0-6.5 N 0.18-0.22; Cu 0.50-1.00
AFNOR NF A 49-217:1987 TU Z 1 CNDU 20 18 06 AZ 0.020 1.00 0.80 0.030 0.010 19.50-20.50 17.50-18.50 6.00-6.50 Cu 0.50-1.00
ASTM A 213/A 213M-03a TP316 S31600 0.08 2.00 0.75 0.040 0.030 16.0-18.0 11.0-14.0 2.00-3.00
ASTM A 249/A 249M-03 TP316 S31600 0.08 2.00 1.00 0.045 0.030 16.0-18.0 10.0-14.0 2.00-3.00
ASTM A 312/A 312M-03 TP316 S31600 0.08 2.00 1.00 0.045 0.030 16.0-18.0 11.0-14.0 2.00-3.00
ASTM A 358/A 358M-01 316 S31600 0.08 2.00 0.75 0.045 0.030 16.0-18.0 10.0-14.0 2.00-3.00 N 0.10
ASTM A 376/A 376M-02a TP316 0.08 2.00 0.75 0.045 0.030 16.0-18.0 11.0-14.0 2.00-3.00
ASTM A 409/A 409M-01 TP316 S31600 0.08 2.00 1.00 0.045 0.030 16.0-18.0 10.0-14.0 2.00-3.00
ASTM A 688/A 688M-03 TP316 S31600 0.08 2.00 0.75 0.040 0.030 16.00-18.00 10.00-14.00 2.00-3.00
JIS G 3459:1997 SUS316TP 0.08 2.00 1.00 0.040 0.030 16.00-18.00 10.00-14.00 2.00-3.00
JIS G 3463:1994 SUS316TB 0.08 2.00 1.00 0.040 0.030 16.00-18.00 10.00-14.00 2.00-3.00
JIS G 3467:1988 SUS 316 TF 0.08 2.00 1.00 0.040 0.030 16.00-18.00 10.00-14.00 2.00-3.00
JIS G 3468:1994 SUS316 0.08 2.00 1.00 0.045 0.030 16.00-18.00 10.00-14.00 2.00-3.00

316S31 0.070 2.00 1.00 0.040 0.030 16.50-18.50 10.50-13.50 2.00-2.50
BS 3605-1:1991 AMD 2:1997
316S33 0.070 2.00 1.00 0.040 0.030 16.50-18.50 11.00-14.00 2.50-3.00
316S31 0.070 2.00 1.00 0.04 0.03 16.50-18.50 10.50-13.50 2.00-2.50
BS 3605-2:1992 AMD 1:1997
316S33 0.070 2.00 1.00 0.04 0.03 16.50-18.50 11.00-14.00 2.50-3.00
DIN 17457:1985 X 5 CrNiMo 17 12 2 1.4401 0.07 16.5-18.5 10.5-13.5 2.0-2.5
DIN 17458:1985 X 5 CrNiMo 17 12 2 1.4401 0.07 16.5-18.5 10.5-13.5 2.0-2.5
DIN 17457:1985 X 5 CrNiMo17 13 3 1.4436 0.07 0.025 16.5-18.5 11.0-14.0 2.5-3.0
DIN 17458:1985 X 5 CrNiMo17 13 3 1.4436 0.07 0.025 16.5-18.5 11.0-14.0 2.5-3.0
DIN 28180:1985 X 5 CrNiMo 17 12 2 1.4401 0.07 16.5-18.5 10.5-13.5 2.0-2.5
DIN 28181:1985 X 5 CrNiMo 17 12 2 1.4401 0.07 16.5-18.5 10.5-13.5 2.0-2.5
AFNOR NF A 49-217:1987 TU Z 6 CND 17 11 0.070 2.00 1.00 0.040 0.030 16.00-18.00 10.00-12.50 2.00-2.40
AFNOR NF A 49-244:1993 X7CrNiMo17-11-2 0.070 2.00 0.75 0.040 0.015 16.0-18.0 10.0-12.0 2.00-2.50
AFNOR NF A 49-247:1981 TS Z 6 CND 17-11 0.070 2.00 1.00 0.040 0.030 16-18.0 10-12.50 2.00-2.40
NOTE: This section continued on next page
Chapter 5 Steel Tubes and Pipes 229


Handbook of Comparative World Steel Standards
5.9 Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures

5.9.2A Chemical Composition of Austenitic Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures (Continued)

Weight, %, max, Unless Otherwise Specified
Standard
Designation
Grade, Class, Type,
Symbol or Name
Steel

Number
UNS
Number
C Mn Si P S Cr Ni Mo Others
TS 60 0.07 2.00 1.00 0.045 0.030 16.00-18.50 11.00-14.00 2.00-2.50
ISO 2604-II:1975
TS 61 0.07 2.00 1.00 0.045 0.030 16.00-18.50 11.00-14.50 2.50-3.00
TW 60 0.07 2.00 1.00 0.045 0.030 16.00-18.50 10.50-14.00 2.00-2.50
ISO 2604-V:1978
TW 61 0.07 2.00 1.00 0.045 0.030 16.00-18.50 11.00-14.50 2.50-3.00
ASTM A 213/A 213M-03a TP316L S31603 0.035 2.00 0.75 0.040 0.030 16.0-18.0 10.0-15.0 2.00-3.00
ASTM A 249/A 249M-03 TP316L S31603 0.030 2.00 1.00 0.045 0.030 16.0-18.0 10.0-14.0 2.00-3.00
ASTM A 312/A 312M-03 TP316L S31603 0.035 2.00 1.00 0.045 0.030 16.0-18.0 10.0-14.0 2.00-3.00
ASTM A 358/A 358M-01 316L S31603 0.030 2.00 0.75 0.045 0.030 16.0-18.0 10.0-14.0 2.00-3.00 N 0.10
ASTM A 409/A 409M-01 TP316L S31603 0.035 2.00 1.00 0.045 0.030 16.0-18.0 10.0-14.0 2.00-3.00
ASTM A 688/A 688M-03 TP316L S31603 0.035 2.00 0.75 0.040 0.030 16.00-18.00 10.00-15.00 2.00-3.00
JIS G 3459:1997 SUS316LTP 0.030 2.00 1.00 0.040 0.030 16.00-18.00 12.00-16.00 2.00-3.00
JIS G 3463:1994 SUS316LTB 0.030 2.00 1.00 0.040 0.030 16.00-18.00 12.00-16.00 2.00-3.00
JIS G 3468:1994 SUS316L 0.030 2.00 1.00 0.045 0.030 16.00-18.00 12.00-15.00 2.00-3.00
316S11 0.030 2.00 1.00 0.040 0.030 16.50-18.50 11.00-14.00 2.00-2.50
BS 3605-1:1991 AMD 2:1997
316S13 0.030 2.00 1.00 0.040 0.030 16.50-18.50 11.50-14.50 2.50-3.00
316S11 0.030 2.00 1.00 0.04 0.03 16.50-18.50 11.00-14.00 2.00-2.50
BS 3605-2:1992 AMD 1:1997
316S13 0.030 2.00 1.00 0.04 0.03 16.50-18.50 11.50-14.50 2.50-3.00
DIN 17457:1985 X 2 CrNiMo 17 13 2 1.4404 0.030 16.5-18.5 11.0-14.0 2.0-2.5
DIN 17458:1985 X 2 CrNiMo 17 13 2 1.4404 0.030 16.5-18.5 11.0-14.0 2.0-2.5
DIN 17457:1985 X 2 CrNiMo 18 14 3 1.4435 0.030 0.025 17.0-18.5 12.5-15.0 2.5-3.0
DIN 17458:1985 X 2 CrNiMo 18 14 3 1.4435 0.030 0.025 17.0-18.5 12.5-15.0 2.5-3.0
AFNOR NF A 49-217:1987 TU Z 2 CND 17 12 0.030 2.00 1.00 0.040 0.030 16.00-18.00 10.50-13.00 2.00-2.40

X3CrNiMo17-11-2 0.030 2.00 0.75 0.040 0.015 16.0-18.0 10.0-12.0 2.00-2.50
X3CrNiMo17-12-3 0.030 2.00 0.75 0.040 0.015 16.5-18.5 11.0-13.0 2.5-3.00
X3CrNiMo18-12-3 0.030 2.00 0.75 0.040 0.015 16.5-18.5 11.0-13.0 2.25-2.75
AFNOR NF A 49-244:1993
TU Z 2 CND 18 14 0.030 2.00 1.00 0.020 0.015 17.00-18.50 13.00-16.00 2.20-3.00
AFNOR NF A 49-247:1981 TS Z 2 CND 17-12 0.030 2.00 1.00 0.040 0.030 16-18.0 10.5-13.00 2.00-2.40
TS 57 0.03 2.00 1.00 0.045 0.030 16.00-18.50 11.00-14.00 2.00-2.50
ISO 2604-II:1975
TS 58 0.03 2.00 1.00 0.045 0.030 16.00-18.50 11.50-14.50 2.50-3.00
TW 57 0.03 2.00 1.00 0.045 0.030 16.00-18.50 11.00-14.00 2.00-2.50
ISO 2604-V:1978
TW 58 0.03 2.00 1.00 0.045 0.030 16.00-18.50 11.50-14.50 2.50-3.00

Chapter 5 Steel Tubes and Pipes 230


Handbook of Comparative World Steel Standards
5.9 Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures

5.9.2A Chemical Composition of Austenitic Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures (Continued)

Weight, %, max, Unless Otherwise Specified
Standard
Designation
Grade, Class, Type,
Symbol or Name
Steel
Number
UNS
Number

C Mn Si P S Cr Ni Mo Others
ASTM A 213/A 213M-03a TP316LN - S31653 0.035 2.00 0.75 0.040 0.030 16.0-18.0 11.0-14.0 2.00-3.00 0.10-0.16
ASTM A 249/A 249M-03 TP316LN S31653 0.080 2.00 1.00 0.045 0.030 16.0-18.0 10.0-13.0 2.00-3.00 N 0.10-0.16
ASTM A 376/A 376M-02a TP316LN 0.035 2.00 0.75 0.045 0.030 16.0-18.0 11.0-14.0 2.00-3.00 N 0.10-0.16
ASTM A 688/A 688M-03 TP316LN S31653 0.035 2.00 0.75 0.040 0.030 16.00-18.00 10.00-15.00 2.00-3.00 N 0.10-0.16
DIN 17457:1985 X 2 CrNiMoN 17 13 3 1.4429 0.030 0.025 16.5-18.5 11.5-14.5 2.5-3.0 N 0.14-0.22
DIN 17458:1985 X 2 CrNiMoN 17 13 3 1.4429 0.030 0.025 16.5-18.5 11.5-14.5 2.5-3.0 N 0.14-0.22
AFNOR NF A 49-217:1987 TU Z 2 CND 17 12 AZ 0.030 2.00 1.00 0.040 0.030 16.00-18.00 11.00-13.50 2.00-2.40 N 0.10-0.20
X3CrNiMoN17-11 0.030 2.00 0.75 0.040 0.015 16.0-18.0 10.0-12.0 2.00-2.5 N 0.12-0.20
AFNOR NF A 49-244:1993
X3CrNiMoN17-12 0.030 2.00 0.75 0.040 0.015 16.0-18.0 11.0-13.0 2.5-3.0 N 0.12-0.20
ASTM A 213/A 213M-03a TP316H S31609 0.04-0.10 2.00 0.75 0.040 0.030 186.0-18.0 11.0-14.0 2.00-3.00
ASTM A 249/A 249M-03 TP316H S31609 0.04-0.10 2.00 1.00 0.045 0.030 16.0-18.0 10.0-14.0 2.00-3.00
ASTM A 312/A 312M-03 TP316H S31609 0.04-0.10 2.00 1.00 0.045 0.030 16.0-18.0 11.0-14.0 2.00-3.00
ASTM A 358/A 358M-01 316H S31609 0.04-0.10 2.00 0.75 0.045 0.030 16.0-18.0 10.0-14.0 2.00-3.00
ASTM A 376/A 376M-02a TP316H S31609 0.04-0.10 2.00 0.75 0.045 0.030 16.0-18.0 11.0-14.0 2.00-3.00
JIS G 3459:1997 SUS316HTP 0.04-0.10 2.00 0.75 0.030 0.030 16.00-18.00 11.00-14.00 2.00-3.00
JIS G 3463:1994 SUS316HTB 0.04-0.10 2.00 0.75 0.030 0.030 16.00-18.00 11.00-14.00 2.00-3.00
JIS G 3467:1988 SUS 316H TF 0.04-0.10 2.00 0.75 0.030 0.030 16.00-18.00 11.00-14.00 2.00-3.00
BS 3605-1:1991 AMD 2:1997 316S51 0.04-0.10 2.00 1.00 0.040 0.030 16.50-18.50 10.50-13.50 2.00-2.50
DIN 17459:1992 X 6 CrNiMo 17 13 1.4919 0.04-0.08 2.0 0.75 0.035 0.015 16.0-18.0 12.0-14.0 2.0-2.5
AFNOR NF A 49-214:1978 Z 6 CND 17-12 B 0.04-0.08 2.0 1.0 0.035 0.030 16-18 11-14 2.0-3.0
ISO 2604-II:1975 TS 63 0.04-0.09 1.00-2.00 0.75 0.045 0.030 16.00-18.00 12.00-14.00 2.00-2.75
BS 3605-1:1991 AMD 2:1997 316S52 0.04-0.10 2.00 1.00 0.040 0.030 16.50-18.50 10.50-13.50 2.00-2.50 B 0.0015-0.006
DIN 17459:1992 X 3 CrNiMoN 17 13 1.4910 0.04 2.0 0.75 0.035 0.015 16.0-18.0 12.0-14.0 2.0-2.8 B 0.0015-0.0050; N 0.10-0.18
JIS G 3459:1997 SUS316TiTP 0.08 2.00 1.00 0.040 0.030 16.00-18.00 10.00-14.00 2.00-3.00 Ti 5 x C min
JIS G 3463:1994 SUS316TiTB 0.08 2.00 1.00 0.040 0.030 16.00-18.00 10.00-1400 2.00-3.00 Ti 5 x C min
DIN 17457:1985 X 6 CrNiMoTi 17 12 2 1.4571 0.08 16.5-18.5 10.5-13.5 2.0-2.5 Ti 5 x C to 0.80
DIN 17458:1985 X 6 CrNiMoTi 17 12 2 1.4571 0.08 16.5-18.5 10.5-13.5 2.0-2.5 Ti 5 x C to 0.80
DIN 28180:1985 X 6 CrNiMoTi 17 12 2 1.4571 0.08 16.5-18.5 10.5-13.5 2.0-2.5 Ti 5 x C to 0.80

DIN 28181:1985 X 6 CrNiMoTi 17 12 2 1.4571 0.08 16.5-18.5 10.5-13.5 2.0-2.5 Ti 5 x C to 0.80
AFNOR NF A 49-214:1978 Z 8 CNDT 17-13 B 0.05-0.10 2.0 1.0 0.035 0.030 16-18 12-15 2.0-3.0 Ti 4 x C to 0.75
AFNOR NF A 49-244:1993 X6CrNiMo17-11-2 0.060 2.00 0.75 0.040 0.015 16.0-18.0 10.5-12.5 2.00-2.5 Ti 5 (C+N) to 0.70; Ti/C+N to 15

Chapter 5 Steel Tubes and Pipes 231


Handbook of Comparative World Steel Standards
5.9 Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures

5.9.2A Chemical Composition of Austenitic Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures (Continued)

Weight, %, max, Unless Otherwise Specified
Standard
Designation
Grade, Class, Type,
Symbol or Name
Steel
Number
UNS
Number
C Mn Si P S Cr Ni Mo Others
ASTM A 213/A 213M-03a TP317 S31700 0.08 2.00 0.75 0.040 0.030 18.0-20.0 11.0-14.0 3.00-4.00
ASTM A 249/A 249M-03 TP317 S31700 0.08 2.00 1.00 0.045 0.030 18.0-20.0 11.0-15.0 3.00-4.00
ASTM A 312/A 312M-03 TP317 S31700 0.08 2.00 1.00 0.045 0.030 18.0-20.0 11.0-14.0 3.0-4.0
ASTM A 409/A 409M-01 TP317 S31700 0.08 2.00 1.00 0.045 0.030 18.0-20.0 11.0-15.0 3.0-4.0
JIS G 3459:1997 SUS317TP 0.08 2.00 1.00 0.040 0.030 18.00-20.00 11.00-15.00 3.00-4.00
JIS G 3463:1994 SUS317TB 0.08 2.00 1.00 0.040 0.030 18.00-20.00 11.00-15.00 3.00-4.00
JIS G 3468:1994 SUS317 0.08 2.00 1.00 0.045 0.030 18.00-20.00 11.00-15.00 3.00-4.00
ASTM A 213/A 213M-03a TP317L S31703 0.035 2.00 0.75 0.040 0.030 18.0-20.0 11.0-15.0 3.00-4.00

ASTM A 249/A 249M-03 TP317L S31703 0.030 2.00 1.00 0.045 0.030 18.0-20.0 11.0-15.0 3.00-4.00
ASTM A 312/A 312M-03 TP317L S31703 0.035 2.00 1.00 0.045 0.030 18.0-20.0 11.0-15.0 3.0-4.0
JIS G 3459:1997 SUS317LTP 0.030 2.00 1.00 0.040 0.030 18.00-20.00 11.00-15.00 3.00-4.00
JIS G 3463:1994 SUS317LTB 0.030 2.00 1.00 0.040 0.030 18.00-20.00 11.00-15.00 3.00-4.00
JIS G 3468:1994 SUS317L 0.030 2.00 1.00 0.045 0.030 18.00-20.00 11.00-15.00 3.00-4.00
AFNOR NF A 49-244:1993 X3CrNiMo19-15-4 0.030 2.00 0.75 0.035 0.010 17.5-19.5 14.0-16.0 3.00-4.00
AFNOR NF A 49-247:1981 TS Z 2 CND 19-15 0.030 2.00 1.00 0.040 0.030 17.5-19.5 14-16 3.0-4.0
ASTM A 213/A 213M-03a TP321 S32100 0.08 2.00 0.75 0.040 0.030 17.0-20.0 9.00-13.0 Ti 5 X C-0.60
ASTM A 249/A 249M-03 TP321 S32100 0.08 2.00 1.00 0.045 0.030 17.0-19.0 9.00-12.0 N 0.10; Ti 5 x (C+N) to 0.70
ASTM A 312/A 312M-03 TP321 S32100 0.08 2.00 1.00 0.045 0.030 17.0-19.0 9.0-12.0 N 0.10; Ti 5 x C to 0.70
ASTM A 358/A 358M-01 321 S32100 0.08 2.00 0.75 0.045 0.030 17.0-19.0 9.0-12.0 Ti 5 x (C+N) to 0.70; N 0.10
ASTM A 376/A 376M-02a TP321 0.08 2.00 0.75 0.045 0.030 17.0-19.0 9.00-13.0 Ti 5 x C to 0.70
ASTM A 409/A 409M-01 TP321 S32100 0.08 2.00 1.00 0.045 0.030 17.0-20.0 9.00-12.0 Ti 5 x C to 0.70
JIS G 3459:1997 SUS321TP 0.08 2.00 1.00 0.040 0.030 17.00-19.00 9.00-13.00 Ti 5 x C min
JIS G 3463:1994 SUS321TB 0.08 2.00 1.00 0.040 0.030 17.00-19.00 9.00-13.00 Ti 5 x C min
JIS G 3467:1988 SUS 321 TF 0.08 2.00 1.00 0.040 0.030 17.00-19.00 9.00-13.00 Ti 5 x C min
JIS G 3468:1994 SUS321 0.08 2.00 1.00 0.045 0.030 17.00-19.00 9.00-13.00 Ti 5 x C min
BS 3605-1:1991 AMD 2:1997 321S31 0.080 2.00 1.00 0.040 0.030 17.00-19.00 9.00-12.00 Ti 5 x C to 0.80
BS 3605-2:1992 AMD 1:1997 321S31 0.080 2.00 1.00 0.04 0.03 17.00-19.00 9.00-12.00 Ti 5 x C to 0.80
DIN 17457:1985 X 6 CrNiTi 18 10 1.4541 0.08 17.0-19.0 9.0-12.0 Ti 5 x C to 0.80
DIN 17458:1985 X 6 CrNiTi 18 10 1.4541 0.08 17.0-19.0 9.0-12.0 Ti 5 x C to 0.80
DIN 28180:1985 X 6 CrNiTi 18 10 1.4541 0.08 17.0-19.0 9.0-12.0 Ti 5 x C to 0.80
DIN 28181:1985 X 6 CrNiTi 18 10 1.4541 0.08 17.0-19.0 9.0-12.0 Ti 5 x C to 0.80
AFNOR NF A 49-217:1987 TU Z 6 CNT 18 10 0.080 2.00 1.00 0.040 0.030 17.00-20.00 9.00-12.00 Ti 5 x C to 0.6
AFNOR NF A 49-244:1993 X6CrNiTi18-10 0.060 2.00 0.75 0.040 0.015 17.0-19.0 9.0-11.0 Ti 5 x (C+N) to 0.70; Ti/C+N to 15
AFNOR NF A 49-247:1981 TS Z 6 CNT 18-10 0.080 2.00 1.00 0.040 0.030 17-20.0 9-12.00 Ti 5 x C to 0.6
ISO 2604-II:1975 TS 53 0.08 2.00 1.00 0.045 0.030 17.00-19.00 9.00-13.00 Ti 5 x C to 0.80
ISO 2604-V:1978 TW 53 0.08 2.00 1.00 0.045 0.030 17.00-19.00 9.00-12.00 Ti 5 x C to 0.80
Chapter 5 Steel Tubes and Pipes 232

Handbook of Comparative World Steel Standards
5.9 Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures

5.9.2A Chemical Composition of Austenitic Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures (Continued)

Weight, %, max, Unless Otherwise Specified
Standard
Designation
Grade, Class, Type,
Symbol or Name
Steel
Number
UNS
Number
C Mn Si P S Cr Ni Mo Others
ASTM A 213/A 213M-03a TP321H S32109 0.04-0.10 2.00 0.75 0.040 0.030 17.0-20.0 9.00-13.0 Ti 4 X C-0.60
ASTM A 249/A 249M-03 TP321H S32109 0.04-0.10 2.00 1.00 0.045 0.030 17.0-19.0 9.00-12.0 N 0.10; Ti 5 x (C+N) to 0.70
ASTM A 312/A 312M-03 TP321H S32109 0.04-0.10 2.00 1.00 0.045 0.030 17.0-19.0 9.0-12.0 Ti 5 x C to 0.60
ASTM A 376/A 376M-02a TP321H S32109 0.04-0.10 2.00 0.75 0.040 0.030 17.0-19.0 9.00-13.0 Ti 4 x C to 0.70
JIS G 3459:1997 SUS321HTP 0.04-0.10 2.00 0.75 0.030 0.030 17.00-20.00 9.00-13.00 Ti 4 x C to 0.60
JIS G 3463:1994 SUS321HTB 0.04-0.10 2.00 0.75 0.030 0.030 17.00-20.00 9.00-13.00 Ti 4 x C to 0.60
JIS G 3467:1988 SUS 321H TF 0.04-0.10 2.00 0.75 0.030 0.030 17.00-20.00 9.00-13.00 Ti 4 x C to 0.60
BS 3605-1:1991 AMD 2:1997 321S51 0.04-0.10 2.00 1.00 0.040 0.030 17.00-19.00 9.00-12.00 Ti 5 x C to 0.80
AFNOR NF A 49-214:1978 Z 6 CNT 18-12 B 0.04-0.08 2.0 1.0 0.035 0.030 17-19 10-13 Ti 4 x C to 0.60
ISO 2604-II:1975 TS 54 0.04-0.10 2.00 0.20-0.80 0.045 0.030 17.00-20.00 9.00-13.00 Ti 4 x C to 0.60
JIS G 3463:1994 SUS329J3LTB 0.030 1.50 1.00 0.040 0.030 21.00-24.00 4.50-6.50 2.50-3.50 N 0.08-0.20
AFNOR NF A 49-217:1987 TU Z 2 CND 22 05 03 0.030 2.00 1.00 0.030 0.020 21.00-23.00 4.50-6.50 2.50-3.50 N 0.08-0.20
JIS G 3463:1994 SUS329J4LTB 0.030 1.50 1.00 0.040 0.030 24.00-26.00 5.50-7.50 2.50-3.50 N 0.08-0.30
AFNOR NF A 49-217:1987 TU Z 2 CND 25 07 03 0.030 1.70 0.70 0.030 0.020 23.50-25.50 5.50-7.50 2.50-3.50 N 0.15-0.25

ASTM A 213/A 213M-03a TP347 S34700 0.08 2.00 0.75 0.040 0.030 17.0-20.0 9.00-13.0 Cb+Ta 10 X C -1.00
ASTM A 249/A 249M-03 TP347 S34700 0.08 2.00 1.00 0.045 0.030 17.0-19.0 9.00-12.0 N 0.40-0.60; Cb 0.10; Cb 10 x C to 1.10
ASTM A 312/A 312M-03 TP347 S34700 0.08 2.00 1.00 0.045 0.030 17.0-19.0 9.0-13.0 Cb 10 x C to 1.00
ASTM A 358/A 358M-01 347 S34700 0.08 2.00 0.75 0.045 0.030 17.0-19.0 9.0-13.0 Cb 10 x C to 1.00
ASTM A 376/A 376M-02a TP347 0.08 2.00 0.75 0.040 0.030 17.0-19.0 9.00-13.0 Cb 10 x C to 1.10
ASTM A 409/A 409M-01 TP347 S34700 0.08 2.00 1.00 0.045 0.030 17.0-19.0 9.00-12.0 (Cb+Ta) 10 x C to 1.10
JIS G 3459:1997 SUS347TP 0.08 2.00 1.00 0.040 0.030 17.00-19.00 9.00-13.00 Nb 10 x C min
JIS G 3463:1994 SUS347TB 0.08 2.00 1.00 0.040 0.030 17.00-19.00 9.00-13.00 Nb 10 x C min
JIS G 3467:1988 SUS 347 TF 0.08 2.00 1.00 0.040 0.030 17.00-19.00 9.00-13.00 Nb 10 x C min
JIS G 3468:1994 SUS347 0.08 2.00 1.00 0.045 0.030 17.00-19.00 9.00-13.00 Nb 10 x C min
BS 3605-1:1991 AMD 2:1997 347S31 0.080 2.00 1.00 0.040 0.030 17.00-19.00 9.00-13.00 Nb 10 x C to 1.00
BS 3605-2:1992 AMD 1:1997 347S31 0.080 2.00 1.00 0.04 0.03 17.00-19.00 9.00-12.00 Nb 10 x C to 1.00
DIN 17457:1985 X 6 CrNiNb 18 10 1.4550 0.08 17.0-19.0 9.0-12.0 Nb 10 x C to 1.00
DIN 17458:1985 X 6 CrNiNb 18 10 1.4550 0.08 17.0-19.0 9.0-12.0 Nb 10 x C to 1.00
ISO 2604-II:1975 TS 50 0.08 2.00 1.00 0.045 0.030 17.00-19.00 9.00-13.00 Nb 10 x C to 1.00
ISO 2604-V:1978 TW 50 0.08 2.00 1.00 0.045 0.030 17.00-19.00 9.00-12.00 Nb 10 x C to 1.00

Chapter 5 Steel Tubes and Pipes 233


Handbook of Comparative World Steel Standards
5.9 Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures

5.9.2A Chemical Composition of Austenitic Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures (Continued)

Weight, %, max, Unless Otherwise Specified
Standard
Designation
Grade, Class, Type,
Symbol or Name

Steel
Number
UNS
Number
C Mn Si P S Cr Ni Mo Others
ASTM A 213/A 213M-03a TP347H S34709 0.04-0.10 2.00 0.75 0.040 0.030 17.0-20.0 9.00-13.0 Cb+Ta 8 X C -1.0
ASTM A 249/A 249M-03 TP347H S34709 0.04-0.10 2.00 1.00 0.045 0.030 17.0-19.0 9.00-12.0 Cb 8 x C to 1.0
ASTM A 312/A 312M-03 TP347H S34709 0.04-0.10 2.00 1.00 0.045 0.030 17.0-19.0 9.0-13.0 Cb 8 x C to 1.00
ASTM A 376/A 376M-02a TP347H S34709 0.04-0.10 2.00 0.75 0.045 0.030 17.0-19.0 9.00-13.0 Cb 8 x C to 1.10
JIS G 3459:1997 SUS347HTP 0.04-0.10 2.00 1.00 0.030 0.030 17.00-20.00 9.00-13.00 Nb 8 x C to 1.00
JIS G 3463:1994 SUS347HTB 0.04-0.10 2.00 1.00 0.030 0.030 17.00-20.00 9.00-13.00 Nb 8 x C to 1.00
JIS G 3467:1988 SUS 347H TF 0.04-0.10 2.00 0.75 0.030 0.030 17.00-20.00 9.00-13.00 Nb 8 x C to 1.00
BS 3605-1:1991 AMD 2:1997 347S51 0.04-0.10 2.00 1.00 0.040 0.030 17.00-19.00 9.00-13.00 Nb 10 x C to 1.20
DIN 17459:1992 X 8 CrNiNb 16 13 1.4961 0.04-0.10 1.5 0.30-0.60 0.035 0.015 15.0-17.0 12.0-14.0 Nb 10 x C to 1.2
AFNOR NF A 49-214:1978 Z 6 CN Nb 18-12 B 0.04-0.08 2.0 1.0 0.035 0.030 17-19 10-13 (Nb+Ta) 8 x C to 1.00
ISO 2604-II:1975 TS 56 0.04-0.10 2.00 0.20-0.80 0.045 0.030 16.00-20.00 11.00-14.00 Nb 10 x C to 1.4
ASTM A 213/A 213M-03a S31725 0.03 2.00 0.75 0.040 0.030 18.0-20.0 13.5-17.5 4.0-5.00 N 0.10; Cu 0.75
ASTM A 249/A 249M-03 S31725 0.03 2.00 1.00 0.045 0.030 18.0-20.0 13.5-17.5 4.0-5.0 N 0.20
ASTM A 312/A 312M-03 S31725 0.03 2.00 1.00 0.040 0.030 18.0-20.0 13.5-17.5 4.0-5.0 N 0.10; Cu 0.75
ASTM A 358/A 358M-01 S31725 0.030 2.00 0.75 0.045 0.030 18.0-20.0 13.5-17.5 4.0-5.0 N 0.20
ASTM A 376/A 376M-02a S31725 0.030 2.00 0.75 0.045 0.030 18.0-20.0 13.5-17.5 4.0-5.0 N 0.20; Cu 0.75
ASTM A 409/A 409M-01 S31725 0.030 2.00 1.00 0.045 0.030 18.0-20.0 13.5-17.5 4.0-5.0 N 0.020
DIN 17457:1985 X 2 CrNiMoN 17 13 5 1.4439 0.030 0.025 16.5-18.5 12.5-14.5 4.0-5.0 N 0.12-0.22
DIN 17458:1985 X 2 CrNiMoN 17 13 5 1.4439 0.030 0.025 16.5-18.5 12.5-14.5 4.0-5.0 N 0.12-0.22
AFNOR NF A 49-244:1993 X3CrNiMoN18-14-5 0.030 2.00 0.75 0.035 0.010 17.0-19.0 13.0-15.0 4.0-5.0 N 0.12-0.20
ASTM A 358/A 358M-01 N08904 0.020 2.00 1.00 0.045 0.035 19.0-23.0 23.0-28.0 4.0-5.0 Cu 1.0-2.0; N 0.10
ASTM A 249/A 249M-03 N08904 0.020 2.00 1.00 0.040 0.030 19.0-23.0 23.0-28.0 4.0-5.0 N 0.10; Cu 1.00-2.00
JIS G 3459:1997 SUS890LTP 0.020 2.00 1.00 0.040 0.030 19.00-23.00 23.00-28.00 4.00-5.00 Cu 1.00-2.00
JIS G 3463:1994 SUS890LTB 0.020 2.00 1.00 0.040 0.030 19.00-23.00 23.00-28.00 4.00-5.00 Cu 1.00-2.00
AFNOR NF A 49-244:1993 X2NiCrMoCu25-20 0.020 2.00 0.40 0.035 0.010 19.0-21.0 24.0-26.0 4.0-5.0 Cu 1.00-2.00

ASTM A 240/A 240M-03c 800 N08800 0.10 1.50 1.00 0.045 0.015 19.0-23.0 30.0-35.0 Cu 0.75; Ti 0.15-0.60
JIS G 3467:1988 NCF 800 TF 0.10 1.50 1.00 0.030 0.015 19.00-23.00 30.00-35.00 Cu 0.75; Al 0.15-0.60; Ti 0.15-0.60
DIN 17459:1992 X 5 NiCrAlTi 31 20 1.4958 0.03-0.08 1.5 0.70 0.015 0.010 19.0-22.0 30.0-32.5 Al 0.20-0.50; Ti 0.20-0.50; Al+Ti 0.70;
AFNOR NF A 49-244:1993 X5NiCr32-21 0.05 1.50 0.75 0.035 0.015 19.0-24.0 30.0-33.0 Al 0.15-0.60; Ti 0.15-0.60
DIN 17459:1992 X 8 NiCrAlTi 32 21 1.4959 0.05-0.10 1.5 0.70 0.015 0.010 19.0-22.0 30.0-34.0 Al 0.25-0.65; Ti 0.25-0.65; Co 0.5;
ASTM A 240/A 240M-03c 800H N08810 0.05-0.10 1.50 1.00 0.045 0.015 19.0-23.0 30.0-35.0 Cu 0.75; Ti 0.15-0.60;
JIS G 3467:1988 NCF 800H TF 0.05-0.10 1.50 1.00 0.030 0.015 19.00-23.00 30.00-35.00 Cu 0.75; Al 0.15-0.60; Ti 0.15-0.60
N08367 0.030 2.00 1.00 0.040 0.030 20.0-22.0 23.5-25.5 6.0-7.0 N 0.18-0.25; Cu 0.75
ASTM A 249/A 249M-03
N08926 0.020 2.00 0.50 0.030 0.010 19.0-21.0 24.0-26.0 6.0-7.0 N 0.15-0.25; Cu 0.50-1.50
ASTM A 312/A 312M-03 N08926 0.020 2.00 0.50 0.030 0.010 24.0-26.0 19.0-21.0 6.0-7.0 N 0.15-0.25; Cu 0.50-1.50
N08367 0.030 2.00 1.00 0.040 0.030 20.00-22.00 23.50-25.50 6.00-7.00 N 0.18-0.25; Cu 0.75
ASTM A 688/A 688M-03
N08926 0.020 2.00 0.5 0.03 0.01 19.00-21.00 24.00-26.00 6.0-7.0 N 0.15-0.25; Cu 0.5-1.5
JIS G 3463:1994 SUS836LTB 0.030 2.00 1.00 0.040 0.030 19.00-24.00 24.00-26.00 5.00-7.00 N 0.25

Chapter 5 Steel Tubes and Pipes 234


Handbook of Comparative World Steel Standards
5.9 Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures

5.9.2B Mechanical Properties of Austenitic Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures

Thickness
Yield Strength, min Tensile Strength, min
Standard
Designation
Grade, Class, Type,
Symbol or Name

Steel
Number
UNS
Number
Product Form/
Heat Treatment
t, mm t, in.
N/mm
2
or
MPa
ksi
N/mm
2
or
MPa
ksi
Elongation,
min, %
Other
ASTM A 213/A 213M-03a TP304 S30400 ST 205
30
515
75
35 95 HRB
ASTM A 249/A 249M-03 TP304 S30400 H + RC 205 30 515 75 35 90 HRB max
ASTM A 312/A 312M-03 TP304 S30400 HF or CF + A 205
30
515
75

35
ASTM A 358/A 358M-01 304 S30400
H, HT, HT-O
or HT-SO
205
30
515
75
40
ASTM A 376/A 376M-02a TP304 see standard 205
30
515
75
35
ASTM A 409/A 409M-01 TP304 S30400
H, HT, HT-O
or HT-SO
205
30
515
75

ASTM A 688/A 688M-03 TP304 S30400 SA 205 30
515
75 35 90 HRB max
JIS G 3459:1997 SUS304TP ST 205

520

35

O.D. < 10 27
10 ≤ O.D. < 20
30
JIS G 3463:1994 SUS304TB ST
O.D. ≥ 20

205 520
35

JIS G 3467:1988 SUS 304 TF ST 205 520 35
JIS G 3468:1994 SUS304 AM 205

520

35
BS 3605-1:1991 AMD 2:1997 304S31 ST or HF 230

490-690

35
BS 3605-2:1992 AMD 1:1997 304S31 AW or ST 230

490-690

35
DIN 17457:1985 X 5 CrNi 18 10 1.4301 SA & Q
≤ 50
195 500-720 40 L; 35 T
L: 85 J at RT
T: 55 J at RT

DIN 17458:1985 X 5 CrNi 18 10 1.4301 SA & Q
≤ 50
195 500-700 40 L; 35 T
L: 85 J at RT
T: 55 J at RT
DIN 28180:1985 X 5 CrNi 18 10 1.4301 SA & Q
≤ 50
195 500-700 40 L; 35 T
L: 85 J at RT
T: 55 J at RT
DIN 28181:1985 X 5 CrNi 18 10 1.4301 SA & Q
≤ 50
195 500-720 40 L; 35 T
85 J at RT, L
55 J at RT, T
AFNOR NF A 49-217:1987 TU Z 6 CN 18 09 HF + CR + Q (HY) 200 490-740 45 90 HRB max
< 3 215 40
3 ≤ t ≤ 5
215 45
AFNOR NF A 49-244:1993 X7CrNi18-9 ST or TT
5 < t ≤ 75
205
520-720
45
L: 90 J at -196°C
T: 70 J at -196°C
AFNOR NF A 49-247:1981 TS Z 6 CN 18-09 Q (HY) 215
530-730
40
ISO 2604-II:1975 TS 47 Q 195 490-690 30

ISO 2604-V:1978 TW 47 Q 195 490-690 30

Chapter 5 Steel Tubes and Pipes 235


Handbook of Comparative World Steel Standards
5.9 Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures

5.9.2B Mechanical Properties of Austenitic Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures (Continued)

Thickness
Yield Strength, min Tensile Strength, min
Standard
Designation
Grade, Class, Type,
Symbol or Name
Steel
Number
UNS
Number
Product Form/
Heat Treatment
t, mm t, in.
N/mm
2
or
MPa
ksi
N/mm
2

or
MPa
ksi
Elongation,
min, %
Other
ASTM A 213/A 213M-03a TP304L S30403 ST 170
25
485
70
35 90 HRB
ASTM A 249/A 249M-03 TP304N S30451 H + RC 240 35 550 80 35 90 HRB max
ASTM A 312/A 312M-03 TP304 L S30403 HF or CF + A 170
25
485
70
35
ASTM A 358/A 358M-01 304L S30403
H, HT, HT-O
or HT-SO
170
25
485
70
40
ASTM A 409/A 409M-01 TP304L S30403
H, HT, HT-O
or HT-SO
170
25

485
70

JIS G 3459:1997 SUS304LTP ST 175

480

35
O.D. < 10 27
10 ≤ O.D. < 20
30
JIS G 3463:1994 SUS304LTB ST
O.D. ≥ 20

175 480
35
JIS G 3468:1994 SUS304L AM 175

480

35
BS 3605-1:1990 Issue 2, 1997 304S11 ST or HF 215

480-680

35
BS 3605-2:1992 AMD 1:1997 304S11 AW or ST 215

480-680

35
DIN 17457:1985 X 2 CrNi 19 11 1.4306 SA & Q
≤ 50
180 460-680 40 L; 35 T
L: 85 J at RT
T: 55 J at RT
DIN 17458:1985 X 2 CrNi 19 11 1.4306 SA & Q
≤ 50
180 460-680 40 L; 35 T
L: 85 J at RT
T: 55 J at RT
AFNOR NF A 49-217:1987 TU Z 2 CN 18 10 HF + CR + Q (HY) 175 470-720 45
90 HRB
100 J at -196°C
< 3 280 40
3 ≤ t ≤ 5
280 45
AFNOR NF A 49-244:1993 X3CrNiN18-10 ST or TT
5 < t ≤ 75
270
570-770
45
L: 100 J at -196°C
T: 80 J at -196°C
AFNOR NF A 49-247:1981 TS Z 2 CN 18-10 Q (HY) 205 520-720 40
ISO 2604-II:1975 TS 46 Q 175
490-690
30
ISO 2604-V:1978 TW 46 Q 175
490-690

30
ASTM A 213/A 213M-03a TP304LN S30453 ST 205
30
515
75
35 90 HRB
ASTM A 249/A 249M-03 TP304LN S30453 H + RC 205 30 515 75 35 90 HRB max
ASTM A 376/A 376M-02a TP304LN see standard 205
30
515
75
35
ASTM A 688/A 688M-03 TP304LN S30453 SA 205 30 515 75 35 90 HRB max
DIN 17457:1985 X 2 CrNiN 18 10 1.4311 SA & Q
≤ 50
270 550-760 35 L; 30 T
L: 85 J at RT
T: 55 J at RT
DIN 17458:1985 X 2 CrNiN 18 10 1.4311 SA & Q
≤ 50
270 550-760 35 L; 30 T
L: 85 J at RT
T: 55 J at RT
AFNOR NF A 49-217:1987 TU Z 2 CN 18 10 AZ 240 550-800 40
NOTE: This section continued on next page

Chapter 5 Steel Tubes and Pipes 236


Handbook of Comparative World Steel Standards

5.9 Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures

5.9.2B Mechanical Properties of Austenitic Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures (Continued)

Thickness
Yield Strength, min Tensile Strength, min
Standard
Designation
Grade, Class, Type,
Symbol or Name
Steel
Number
UNS
Number
Product Form/
Heat Treatment
t, mm t, in.
N/mm
2
or
MPa
ksi
N/mm
2
or
MPa
ksi
Elongation,
min, %
Other

< 3 280 40
3 ≤ t ≤ 5
280 45
X3CrNiN18-10 ST or TT
5 < t ≤ 75
270
570-770
45
L: 100 J at -196°C
T: 80 J at -196°C
< 3 300 35
3 ≤ t ≤ 5
300 40
AFNOR NF A 49-244:1993
X6CrNiN19-9 ST or TT
5 < t ≤ 75
290
590-790
40
L: 100 J at -196°C
T: 80 J at -196°C
ASTM A 213/A 213M-03a TP304H S30409 ST 205
30
515
75
35 90 HRB
ASTM A 249/A 249M-03 TP304H S30409 ST 205 30 515 75 35 90 HRB max
ASTM A 312/A 312M-03 TP304H S30409 HF or CF + A 205
30
515

75
35
ASTM A 358/A 358M-01 304H S30409
H, HT, HT-O
or HT-SO
205
30
515
75
40
ASTM A 376/A 376M-02a TP304H S30409 see standard 205
30
515
75
35
JIS G 3459:1997 SUS304HTP ST 205

520

35
O.D. < 10 27
10 ≤ O.D. < 20
30
JIS G 3463:1994 SUS304HTB ST
O.D. ≥ 20

205 520
35
JIS G 3467:1988 SUS 304H TF ST 205 520 35
BS 3605-1:1990 Issue 2, 1997 304S51 ST or HF 230

490-690

35
DIN 17459:1992 X 6 CrNi 18 11 1.4948 SHT
≤ 50
185 500-700 40 L; 30 T
L: 90 J at RT
T: 60 J at RT
AFNOR NF A 49-214:1978 Z 6 CN 19-10 L or F/H + RC 195 490-690 40
ISO 2604-II:1975 TS 48 Q 195
490-690
30
ASTM A 249/A 249M-03 S30615 H + RC 275 40 620 90 35 95 HRB max
AFNOR NF A 49-217:1987 TU Z 1 CNS 18 15 HF + CR + Q (HY) 220 540-740 40
ASTM A 213/A 213M-03a TP309S S30908 ST 205
30
515
75
35 90 HRB
ASTM A 249/A 249M-03 TP309S S30908 H + RC 205 30 515 75 35 90 HRB max
ASTM A 312/A 312M-03 TP309S S30908 HF or CF + A 205
30
515
75
35
ASTM A 358/A 358M-01 309S S30908
H, HT, HT-O
or HT-SO
205

30
515
75
40
JIS G 3459:1997 SUS309STP ST 205

520

35
O.D. < 10 27
10 ≤ O.D. < 20
30
JIS G 3463:1994 SUS309STB ST
O.D. ≥ 20

205 520
35



JIS G 3468:1994 SUS309S AM 205

520

35
Chapter 5 Steel Tubes and Pipes 237


Handbook of Comparative World Steel Standards
5.9 Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures

5.9.2B Mechanical Properties of Austenitic Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures (Continued)

Thickness
Yield Strength, min Tensile Strength, min
Standard
Designation
Grade, Class, Type,
Symbol or Name
Steel
Number
UNS
Number
Product Form/
Heat Treatment
t, mm t, in.
N/mm
2
or
MPa
ksi
N/mm
2
or
MPa
ksi
Elongation,
min, %
Other
ASTM A 213/A 213M-03a TP309H S30909 ST 205

30
515
75
35 90 HRB
ASTM A 249/A 249M-03 TP309H S30909 ST 205 30 515 75 35 90 HRB max
JIS G 3459:1997 SUS309TP ST 205

520

35
O.D. < 10 27
10 ≤ O.D. < 20
30
JIS G 3463:1994 SUS309TB ST
O.D. ≥ 20

205 520
35
< 3 240 30
3 ≤ t ≤ 5
240 35
AFNOR NF A 49-244:1993 X15CrNi24-13 ST or TT
5 < t ≤ 75
240
540-740
35

ASTM A 213/A 213M-03a TP310S S31008 ST 205
30
515

75
35 90 HRB
ASTM A 249/A 249M-03 TP310S S31008 H + RC 205 30 515 75 35 90 HRB max
ASTM A 312/A 312M-03 TP310S S31008 HF or CF + A 205
30
515
75
35
ASTM A 358/A 358M-01 310S S31008
H, HT, HT-O
or HT-SO
205
30
515
75
40
JIS G 3459:1997 SUS310STP ST 205

520

35
O.D. < 10 27
10 ≤ O.D. < 20
30
JIS G 3463:1994 SUS310STB ST
O.D. ≥ 20

205 520
35

JIS G 3468:1994 SUS310S AM 205

520

35
ASTM A 213/A 213M-03a TP310H S31009 ST 205
30
515
75
35 90 HRB
< 3 205 35
3 ≤ t ≤ 5
205 40
AFNOR NF A 49-244:1993 X1CrNi25-20 ST or TT
5 < t ≤ 75
205
480-680
40
L: 90 J at -196°C
T: 70 J at -196°C
O.D. < 10 27
10 ≤ O.D. < 20
30
JIS G 3463:1994 SUS310TB ST
O.D. ≥ 20

205 520
35

JIS G 3467:1988 SUS 310 TF ST 205 520 35
ISO 2604-II:1975 TS 68 Q 205
510-710
30

t ≤ 0.25
270 39 580 84 25 95 HRB max
ASTM A 249/A 249M-03 S31050 H + RC

t > 0.25
255 37 540 78 25 95 HRB max
AFNOR NF A 49-217:1987 TU Z 1 CND 25 22 AZ HF + CR + Q (HY) 260 540-740 30

t ≤ 0.187
310 45 675 98
ASTM A 249/A 249M-03 S31254 H + WQ or RC

t > 0.187
300 45 655 95
35 100 HRB max

t ≤ 0.187
310 45 690 100 35
ASTM A 688/A 688M-03 S31254 H + WQ or RC

t > 0.187
310 45 655 95 35

90 HRB max
AFNOR NF A 49-217:1987 TU Z 1 CNDU 20 18 06 AZ HF + CR + Q (HY) 300 650-850 35

Chapter 5 Steel Tubes and Pipes 238


Handbook of Comparative World Steel Standards
5.9 Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures

5.9.2B Mechanical Properties of Austenitic Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures (Continued)

Thickness
Yield Strength, min Tensile Strength, min
Standard
Designation
Grade, Class, Type,
Symbol or Name
Steel
Number
UNS
Number
Product Form/
Heat Treatment
t, mm t, in.
N/mm
2
or
MPa
ksi
N/mm

2
or
MPa
ksi
Elongation,
min, %
Other
ASTM A 213/A 213M-03a TP316 S31600 ST 205
30
515
75
35 90
ASTM A 249/A 249M-03 TP316 S31600 H + RC 205 30 515 75 35 90 HRB max
ASTM A 312/A 312M-03 TP316 S31600 HF or CF + A 205
30
515
75
35
ASTM A 358/A 358M-01 316 S31600
H, HT, HT-O
or HT-SO
205
30
515
75
40
ASTM A 376/A 376M-02a TP316 see standard 205
30
515
75

35
ASTM A 409/A 409M-01 TP316 S31600
H, HT, HT-O
or HT-SO
205
30
515
75

ASTM A 688/A 688M-03 TP316 S31600 SA 205 30 515 75 35 90 HRB max
JIS G 3459:1997 SUS316TP ST 205

520

35
O.D. < 10 27
10 ≤ O.D. < 20
30
JIS G 3463:1994 SUS316TB ST
O.D. ≥ 20

205 520
35



JIS G 3467:1988 SUS 316 TF ST 205 520 35
JIS G 3468:1994 SUS316 AM 205

520

35
316S31 ST or HF 240

510-710

35
BS 3605-1:1990 Issue 2, 1997
316S33 ST or HF 240

510-710

35
316S31 AW or ST 240

510-710

35
BS 3605-2:1992 AMD 1:1997
316S33 AW or ST 240

510-710

35
DIN 17457:1985 X 5 CrNiMo 17 12 2 1.4401 SA & Q
≤ 50
205 510-710 40 L; 35 T
L: 85 J at RT
T: 55 J at RT
DIN 17458:1985 X 5 CrNiMo 17 12 2 1.4401 SA & Q

≤ 50
205 510-710 40 L; 30 T
L: 85 J at RT
T: 55 J at RT
DIN 17457:1985 X 5 CrNiMo17 13 3 1.4436 SA & Q
≤ 50
205 510-710 40 L; 35 T
L: 85 J at RT
T: 55 J at RT
DIN 17458:1985 X 5 CrNiMo17 13 3 1.4436 SA & Q
≤ 50
205 510-710 40 L; 30 T
L: 85 J at RT
T: 55 J at RT
DIN 28180:1985 X 5 CrNiMo 17 12 2 1.4401 SA & Q
≤ 50
205 510-710 40 L; 30 T
L: 85 J at RT
T: 55 J at RT
DIN 28181:1985 X 5 CrNiMo 17 12 2 1.4401 SA & Q
≤ 50
205 510-710 40 L; 30 T
L: 85 J at RT
T: 55 J at RT
AFNOR NF A 49-217:1987 TU Z 6 CND 17 11 HF + CR + Q (HY) 190 490-740 45 90 HRB max
< 3 225 40
3 ≤ t ≤ 5
225 45
AFNOR NF A 49-244:1993 X7CrNiMo17-11-2 ST or TT
5 < t ≤ 75

215
540-740
45
L: 90 J at -196°C
T: 70 J at -196°C
AFNOR NF A 49-247:1981 TS Z 6 CND 17-11 Q (HY) 225

540-740

40
TS 60 Q 205
510-710
30
ISO 2604-II:1975
TS 61 Q 205 510-710 30
TW 60 Q 205
510-710
30
ISO 2604-V:1978
TW 61 Q 205 510-710 30
Chapter 5 Steel Tubes and Pipes 239


Handbook of Comparative World Steel Standards
5.9 Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures

5.9.2B Mechanical Properties of Austenitic Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures (Continued)

Thickness
Yield Strength, min Tensile Strength, min

Standard
Designation
Grade, Class, Type,
Symbol or Name
Steel
Number
UNS
Number
Product Form/
Heat Treatment
t, mm t, in.
N/mm
2
or
MPa
ksi
N/mm
2
or
MPa
ksi
Elongation,
min, %
Other
ASTM A 213/A 213M-03a TP316L S31603 ST 170
25
485
70
35 90 HRB
ASTM A 249/A 249M-03 TP316L S31603 H + RC 170 25 485 70 35 90 HRB max

ASTM A 312/A 312M-03 TP316L S31603 HF or CF + A 170
25
485
70
35
ASTM A 358/A 358M-01 316L S31603
H, HT, HT-O
or HT-SO
170
25
485
70
40
ASTM A 409/A 409M-01 TP316L S31603
H, HT, HT-O
or HT-SO
170
25
485
70

ASTM A 688/A 688M-03 TP316L S31603 SA 175 25 485 70 35 90 HRB max
JIS G 3459:1997 SUS316LTP ST 175

480

35
O.D. < 10 27
10 ≤ O.D. < 20
30

JIS G 3463:1994 SUS316LTB ST
O.D. ≥ 20

175 480
35



JIS G 3468:1994 SUS316L AM 175

480

35
316S11 ST or HF 225

490-690

35
BS 3605-1:1990 Issue 2, 1997
316S13 ST or HF 225

490-690

35
316S11 AW or ST 225

490-690

35
BS 3605-2:1992 AMD 1:1997

316S13 AW or ST 225

490-690

35
DIN 17457:1985 X 2 CrNiMo 17 13 2 1.4404 SA & Q
≤ 50
190 490-690 40 L; 35 T
L: 85 J at RT
T: 55 J at RT
DIN 17458:1985 X 2 CrNiMo 17 13 2 1.4404 SA & Q
≤ 50
190 490-690 40 L; 30 T
L: 85 J at RT
T: 55 J at RT
DIN 17457:1985 X 2 CrNiMo 18 14 3 1.4435 SA & Q
≤ 50
190 490-690 40 L; 35 T
L: 85 J at RT
T: 55 J at RT
DIN 17458:1985 X 2 CrNiMo 18 14 3 1.4435 SA & Q
≤ 50
190 490-690 40 L; 30 T
L: 85 J at RT
T: 55 J at RT
AFNOR NF A 49-217:1987 TU Z 2 CND 17 12 HF + CF + Q (HY) 175 470-720 45 90 HRB max
< 3 215 40
3 ≤ t ≤ 5
215 45
X3CrNiMo17-11-2 ST or TT

5 < t ≤ 75
205
510-710
45
L: 90 J at -196°C
T: 70 J at -196°C
< 3 215 40
3 ≤ t ≤ 5
215 45
X3CrNiMo17-12-3 ST or TT
5 < t ≤ 75
205
510-710
45
L: 90 J at -196°C
T: 70 J at -196°C
< 3 215 40
3 ≤ t ≤ 5
215 45
X3CrNiMo18-12-3 ST or TT
5 < t ≤ 75
205
510-710
45
L: 90 J at -196°C
T: 70 J at -196°C
AFNOR NF A 49-244:1993
TU Z 2 CND 18 14 HF + CF + Q (HY) 210 490-690 45
AFNOR NF A 49-247:1981 TS Z 2 CND 17-12 Q (HY) 215

520-720

40
TS 57 Q 185
490-690
30
ISO 2604-II:1975
TS 58 Q 185 490-690 30
TW 57 Q 185
490-690
30
ISO 2604-V:1978
TW 58 Q 185 490-690 30
Chapter 5 Steel Tubes and Pipes 240


Handbook of Comparative World Steel Standards
5.9 Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures

5.9.2B Mechanical Properties of Austenitic Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures (Continued)

Thickness
Yield Strength, min Tensile Strength, min
Standard
Designation
Grade, Class, Type,
Symbol or Name
Steel
Number
UNS

Number
Product Form/
Heat Treatment
t, mm t, in.
N/mm
2
or
MPa
ksi
N/mm
2
or
MPa
ksi
Elongation,
min, %
Other
ASTM A 213/A 213M-03a TP316LN S31653 ST 205
30
515
75
35 90 HRB
ASTM A 249/A 249M-03 TP316LN S31653 H + RC 205 30 515 75 35 90 HRB max
ASTM A 376/A 376M-02a TP316LN see standard 205
30
515
75
35
ASTM A 688/A 688M-03 TP316LN S31653 SA 205 30 515 75 35 90 HRB max
DIN 17457:1985 X 2 CrNiMoN 17 13 3 1.4429 SA & Q

≤ 50
295 580-800 35 L; 30 T
L: 85 J at RT
T: 55 J at RT
DIN 17458:1985 X 2 CrNiMoN 17 13 3 1.4429 SA & Q
≤ 50
295 580-800 35 L; 30 T
L: 85 J at RT
T: 55 J at RT
AFNOR NF A 49-217:1987 TU Z 2 CND 17 12 AZ
HF + CF +
Q (HY)
280 600-800 40
< 3 290 35
3 ≤ t ≤ 5
290 40
X3CrNiMoN17-11 ST or TT
5 < t ≤ 75
290
590-790
40
L: 100 J at -196°C
T: 80 J at -196°C
< 3 290 35
3 ≤ t ≤ 5
290 40
AFNOR NF A 49-244:1993
X3CrNiMoN17-12 ST or TT
5 < t ≤ 75
290

590-790
40
L: 100 J at -196°C
T: 80 J at -196°C
ASTM A 213/A 213M-03a TP316H S31609 ST 205
30
515
75
35 90 HRB
ASTM A 249/A 249M-03 TP316H S31609 ST 205 30 515 75 35 90 HRB max
ASTM A 312/A 312M-03 TP316H S31609
HF or CF
+ A
205
30
515
75
35
ASTM A 358/A 358M-01 316H S31609
H, HT, HT-O
or HT-SO
205
30
515
75
40
ASTM A 376/A 376M-02a TP316H S31609 see standard 205
30
515
75

35
JIS G 3459:1997 SUS316HTP ST 205

520

35
O.D. < 10 27
10 ≤ O.D. < 20
30
JIS G 3463:1994 SUS316HTB ST
O.D. ≥ 20

205 520
35



JIS G 3467:1988 SUS 316H TF ST 205 520 35
BS 3605-1:1990 Issue 2, 1997 316S51 ST or HF 240

510-710

35
DIN 17459:1992 X 6 CrNiMo 17 13 1.4919 SHT
≤ 50
205 490-690 35 L; 30 T
L: 90 J at RT
T: 60 J at RT
AFNOR NF A 49-214:1978 Z 6 CND 17-12 B L or F/H + RC 195 490-690 40
ISO 2604-II:1975 TS 63 Q 205

510-710
30
BS 3605-1:1990 Issue 2, 1997 316S52 ST or HF 240

510-710

35
DIN 17459:1992 X 3 CrNiMoN 17 13 1.4910 SHT
≤ 50
260 550-750 35 L; 30 T
L: 120 J at RT
T: 80 J at RT

Chapter 5 Steel Tubes and Pipes 241


Handbook of Comparative World Steel Standards
5.9 Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures

5.9.2B Mechanical Properties of Austenitic Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures (Continued)

Thickness
Yield Strength, min Tensile Strength, min
Standard
Designation
Grade, Class, Type,
Symbol or Name
Steel
Number
UNS

Number
Product Form/
Heat Treatment
t, mm t, in.
N/mm
2
or
MPa
ksi
N/mm
2
or
MPa
ksi
Elongation,
min, %
Other
JIS G 3459:1997 SUS316TiTP ST 205

520

35
O.D. < 10 27
10 ≤ O.D. < 20
30
JIS G 3463:1994 SUS316TiTB ST
O.D. ≥ 20

205 520
35

DIN 17457:1985 X 6 CrNiMoTi 17 12 2 1.4571 SA & Q
≤ 50
210 500-730 35 L; 30 T
L: 85 J at RT
T: 55 J at RT
≤ 50
210 500-730 35 L; 30 T
L: 85 J at RT
T: 55 J at RT
DIN 17458:1985 X 6 CrNiMoTi 17 12 2 1.4571 SA & Q
≤ 50
190 490-690 35 L; 30 T
L: 85 J at RT
T: 55 J at RT
SA & Q
≤ 50
210 500-730 35 L; 30 T
L: 85 J at RT
T: 55 J at RT
DIN 28180:1985 X 6 CrNiMoTi 17 12 2 1.4571
SA & Q
≤ 50
190 490-690 35 L; 30 T
L: 85 J at RT
T: 55 J at RT
DIN 28181:1985 X 6 CrNiMoTi 17 12 2 1.4571 SA & Q
≤ 50

210 500-730 35 L; 30 T
L: 85 J at RT
T: 55 J at RT
AFNOR NF A 49-214:1978 Z 8 CNDT 17-13 B L or F/H + RC 195 540-740 40
< 3 225 35
3 ≤ t ≤ 5
225 40
AFNOR NF A 49-244:1993 X6CrNiMo17-11-2 ST or TT
5 < t ≤ 75
215
540-740
40
L: 90 J at -196°C
T: 70 J at -196°C
ASTM A 213/A 213M-03a TP317 S31700 ST 205 30 515 75
35
90 HRB
ASTM A 249/A 249M-03 TP317 S31700 H + RC 205 30 515 75 35 90 HRB max
ASTM A 312/A 312M-03 TP317 S31700 HF or CF + A 205
30
515
75
35
ASTM A 409/A 409M-01 TP317 S31700
H, HT, HT-O
or HT-SO
205
30
515
75

JIS G 3459:1997 SUS317TP ST 205

520

35
O.D. < 10 27
10 ≤ O.D. < 20
30
JIS G 3463:1994 SUS317TB ST
O.D. ≥ 20

205 520
35



JIS G 3468:1994 SUS317 AM 205

520

35
ASTM A 213/A 213M-03a TP317L S31703 ST 205
30
515
75
35 90 HRB
ASTM A 249/A 249M-03 TP317L S31703 H + RC 205 30 515 75 35 90 HRB max
ASTM A 312/A 312M-03 TP317L S31703 HF or CF + A 205
30

515
75
35
JIS G 3459:1997 SUS317LTP ST 175

480

35
O.D. < 10 27
10 ≤ O.D. < 20
30
JIS G 3463:1994 SUS317LTB ST
O.D. ≥ 20

175 480
35



JIS G 3468:1994 SUS317L AM 175

480

35
NOTE: This section continued on next page
Chapter 5 Steel Tubes and Pipes 242


Handbook of Comparative World Steel Standards
5.9 Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures

5.9.2B Mechanical Properties of Austenitic Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures (Continued)

Thickness
Yield Strength, min Tensile Strength, min
Standard
Designation
Grade, Class, Type,
Symbol or Name
Steel
Number
UNS
Number
Product Form/
Heat Treatment
t, mm t, in.
N/mm
2
or
MPa
ksi
N/mm
2
or
MPa
ksi
Elongation,
min, %
Other
< 3 215 40

3 ≤ t ≤ 5
215 45
AFNOR NF A 49-244:1993 X3CrNiMo19-15-4 ST or TT
5 < t ≤ 75
205
510-710
45
L: 90 J at -196°C
T: 70 J at -196°C
AFNOR NF A 49-247:1981 TS Z 2 CND 19-15 Q (HY) 225

520-720

35
ASTM A 213/A 213M-03a TP321 S32100 ST 205
30
515
75
35 90 HRB
ASTM A 249/A 249M-03 TP321 S32100 H + RC 205 30 515 75 35 90 HRB max
ASTM A 312/A 312M-03 TP321 Seamless S32100 A
≤ ³⁄₈
205
30
515
75
35
ASTM A 358/A 358M-01 321 S32100
H, HT, HT-O
or HT-SO

205
30
515
75
40
ASTM A 376/A 376M-02a TP321 see standard
≤ ³⁄₈
205
30
515
75
35
ASTM A 409/A 409M-01 TP321 S32100
H, HT, HT-O
or HT-SO
205
30
515
75

JIS G 3459:1997 SUS321TP ST 205

520

35
O.D. < 10 27
10 ≤ O.D. < 20
30
JIS G 3463:1994 SUS321TB ST
O.D. ≥ 20

205 520
35



JIS G 3467:1988 SUS 321 TF ST 205 520 35
JIS G 3468:1994 SUS321 AM 205

520

35
BS 3605-1:1990 Issue 2, 1997 321S31 ST or HF 235

510-710

35
BS 3605-2:1992 AMD 1:1997 321S31 AW or ST 235

510-710

35
DIN 17457:1985 X 6 CrNiTi 18 10 1.4541 SA & Q
≤ 50
200 500-730 35 L; 30 T
L: 85 J at RT
T: 55 J at RT
≤ 50
200 500-730 35 L; 30 T
L: 85 J at RT

T: 55 J at RT
DIN 17458:1985 X 6 CrNiTi 18 10 1.4541 SA & Q
≤ 50
180 460-680 35 L; 30 T
L: 85 J at RT
T: 55 J at RT
SA & Q
≤ 50
200 500-730 35 L; 30 T
L: 85 J at RT
T: 55 J at RT
DIN 28180:1985 X 6 CrNiTi 18 10 1.4541
SA & Q
≤ 50
180 460-680 35 L; 30 T
L: 85 J at RT
T: 55 J at RT
DIN 28181:1985 X 6 CrNiTi 18 10 1.4541 SA & Q
≤ 50
200 500-730 35 L; 30 T
L: 85 J at RT
T: 55 J at RT
AFNOR NF A 49-217:1987 TU Z 6 CNT 18 10 HF + CR + Q (HY) 190 490-740 45 90 HRB max
< 3 220 35
3 ≤ t ≤ 5
220 40
AFNOR NF A 49-244:1993 X6CrNiTi18-10 ST or TT
5 < t ≤ 75
210
530-730

40
L: 90 J at -196°C
T: 70 J at -196°C
AFNOR NF A 49-247:1981 TS Z 6 CNT 18-10 Q (HY) 220

530-730

35
ISO 2604-II:1975 TS 53 Q 195
510-710
30
ISO 2604-V:1978 TW 53 Q 195
510-710
30
Chapter 5 Steel Tubes and Pipes 243


Handbook of Comparative World Steel Standards
5.9 Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures

5.9.2B Mechanical Properties of Austenitic Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures (Continued)

Thickness
Yield Strength, min Tensile Strength, min
Standard
Designation
Grade, Class, Type,
Symbol or Name
Steel
Number

UNS
Number
Product Form/
Heat Treatment
t, mm t, in.
N/mm
2
or
MPa
ksi
N/mm
2
or
MPa
ksi
Elongation,
min, %
Other
ASTM A 213/A 213M-03a TP321H S32109 ST 205
30
515
75
35 90 HRB
ASTM A 249/A 249M-03 TP321H S32109 ST 205 30 515 75 35 90 HRB max
ASTM A 312/A 312M-03 TP321H Welded S32109 HF or CF + A 205
30
515
75
35

≤ ³⁄₈
205
30
515
75
35
ASTM A 376/A 376M-02a TP321H S32109 see standard

> ³⁄₈
170
25
480
70
35
JIS G 3459:1997 SUS321HTP CF or HF + ST 205

520

35
O.D. < 10 27
10 ≤ O.D. < 20
30
JIS G 3463:1994 SUS321HTB ST
O.D. ≥ 20

205 520
35

JIS G 3467:1988 SUS 321H TF CF or HF,ST 205 520 35
BS 3605-1:1990 Issue 2, 1997 321S51 ST or HF 235

510-710

35
AFNOR NF A 49-214:1978 Z 6 CNT 18-12 B L or F/H + RC 195 490-690 40
ISO 2604-II:1975 TS 54 Q 155
490-690
30
O.D. < 10 10
10 ≤ O.D. < 20
13
JIS G 3463:1994 SUS329J3LTB ST
O.D. ≥ 20

450 620
18



AFNOR NF A 49-217:1987 TU Z 2 CND 22 05 03 HF + CR + Q (HY) 450 680-880 25
O.D. < 10 10
10 ≤ O.D. < 20
13
JIS G 3463:1994 SUS329J4LTB ST
O.D. ≥ 20

450 620
18

AFNOR NF A 49-217:1987 TU Z 2 CND 25 07 03 HF + CR + Q (HY) 450 700-900 25
ASTM A 213/A 213M-03a TP347 S34700 ST 205
30
515
75
35 90 HRB
ASTM A 249/A 249M-03 TP347 S34700 H + RC 205 30 515 75 35 90 HRB max
ASTM A 312/A 312M-03 TP347 S34700 HF or CF + A 205
30
515
75
35
ASTM A 358/A 358M-01 347 S34700
H, HT, HT-O
or HT-SO
205
30
515
75
40
ASTM A 376/A 376M-02a TP347 S34700 see standard 205
30
515
75
35
ASTM A 409/A 409M-01 TP347 S34700
H, HT, HT-O

or HT-SO
205
30
515
75

JIS G 3459:1997 SUS347TP ST 205

520

35
O.D. < 10 27
10 ≤ O.D. < 20
30
JIS G 3463:1994 SUS347TB ST
O.D. ≥ 20

205 520
35



JIS G 3467:1988 SUS 347 TF ST 205 520 35
JIS G 3468:1994 SUS347 AM 205

520

35
BS 3605-1:1990 Issue 2, 1997 347S31 ST or HF 240

510-710

35
BS 3605-2:1990 Issue 2, 1997 347S31 ST 240

510-710

35
NOTE: This section continued on next page
Chapter 5 Steel Tubes and Pipes 244


Handbook of Comparative World Steel Standards
5.9 Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures

5.9.2B Mechanical Properties of Austenitic Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures (Continued)

Thickness
Yield Strength, min Tensile Strength, min
Standard
Designation
Grade, Class, Type,
Symbol or Name
Steel
Number
UNS
Number
Product Form/
Heat Treatment
t, mm t, in.

N/mm
2
or
MPa
ksi
N/mm
2
or
MPa
ksi
Elongation,
min, %
Other
DIN 17457:1985 X 6 CrNiNb 18 10 1.4550 SA & Q
≤ 50
205 510-740 35 L; 30 T
L: 85 J at RT
T: 55 J at RT
DIN 17458:1985 X 6 CrNiNb 18 10 1.4550 SA & Q
≤ 50
205 510-740 35 L; 30 T
L: 85 J at RT
T: 55 J at RT
ISO 2604-II:1975 TS 50 Q 205
510-710
30
ISO 2604-V:1978 TW 50 Q 205
510-710
30
ASTM A 213/A 213M-03a TP347H S34709 ST 205

30
515
75
35 90 HRB
ASTM A 249/A 249M-03 TP347H S34709 ST 205 30 515 75 35 90 HRB max
ASTM A 312/A 312M-03 TP347H S34709 HF or CF + A 205
30
515
75
35
ASTM A 376/A 376M-02a TP347H S34709 see standard 205
30
515
75
35
JIS G 3459:1997 SUS347HTP CF or HF + ST 205

520

35
O.D. < 10 27
10 ≤ O.D. < 20
30
JIS G 3463:1994 SUS347HTB ST
O.D. ≥ 20

205 520
35

JIS G 3467:1988 SUS 347H TF CF or HF, ST 205 520 35
BS 3605-1:1990 Issue 2, 1997 347S51 ST or HF 240

510-710

35
DIN 17459:1992 X 8 CrNiNb 16 13 1.4961 SHT
≤ 50
205 510-690 35 L; 22 T
65 J at RT, L
45 J at RT, T
AFNOR NF A 49-214:1978 Z 6 CN Nb 18-12 B L or F/H + RC 195 490-690 40
ISO 2604-II:1975 TS 56 Q 205
510-710
30
ASTM A 213/A 213M-03a S31725 ST 205
30
515
75
35 90 HRB
ASTM A 249/A 249M-03 S31725 ST 205
30
515
75
35 90 HRB
ASTM A 312/A 312M-03 S31725 SA 205
30
515
75

ASTM A 358/A 358-01 S31725 see standard 205
30
515
75

ASTM A 376/A 376M-02a S31725 HT 205
30
515
75 35

ASTM A 409/A 409M-01 S31725
H, HT, HT-O
or HT-SO
205
30
515
75

DIN 17457:1985 X 2 CrNiMoN 17 13 5 1.4439 SA & Q
≤ 50
285 580-800 35 L; 30 T
L: 85 J at RT
T: 55 J at RT
DIN 17458:1985 X 2 CrNiMoN 17 13 5 1.4439 SA & Q
≤ 50
285 580-800 35 L; 30 T
L: 85 J at RT
T: 55 J at RT
< 3 290 35

3 ≤ t ≤ 5
290 40
AFNOR NF A 49-244:1993 X3CrNiMoN18-14-5 ST or TT
5 < t ≤ 75
280
580-780
40
L: 100 J at -196°C
T: 80 J at -196°C

Chapter 5 Steel Tubes and Pipes 245


Handbook of Comparative World Steel Standards
5.9 Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures

5.9.2B Mechanical Properties of Austenitic Stainless Steel Tubes and Pipes for Pressure Purposes and High Temperatures (Continued)

Thickness
Yield Strength, min Tensile Strength, min
Standard
Designation
Grade, Class, Type,
Symbol or Name
Steel
Number
UNS
Number
Product Form/
Heat Treatment

t, mm t, in.
N/mm
2
or
MPa
ksi
N/mm
2
or
MPa
ksi
Elongation,
min, %
Other
ASTM A 358/A 358M-01 N08904
H, HT, HT-O
or HT-SO
220
31
490
71
35
ASTM A 249/A 249M-03 N08904 H + WQ or RC 215 31 490 71 35 90 HRB max
JIS G 3459:1997 SUS890LTP ST 215

490

35
O.D. < 10 27
10 ≤ O.D. < 20

30
JIS G 3463:1994 SUS890LTB ST
O.D. ≥ 20

215 490
35



< 3 230 30
3 ≤ t ≤ 5
230 35
AFNOR NF A 49-244:1993 X2NiCrMoCu25-20 ST or TT
5 < t ≤ 75
230
530-730
35
L: 90 J at -196°C
T: 70 J at -196°C
ASTM A 240/A 240M-03c 800 N08800 205
30
520
75
30
CF, A 205

520

30
JIS G 3467:1988 NCF 800 TF

HF, A 175

450

30
X 5 NiCrAlTi 31 20 RK
1.4958
RK
A/R
≤ 50
210 500-750 35 L; 30 T
L: 120 J at RT
T: 80 J at RT
DIN 17459:1992
X 5 NiCrAlTi 31 20 1.4958 SHT
≤ 50
170 500-750 35 L; 30 T
L: 120 J at RT
T: 80 J at RT
< 3 200 25
3 ≤ t ≤ 5
200 30
AFNOR NF A 49-244:1993 X5NiCr32-21 ST or TT
5 < t ≤ 75
200
490-690
30

DIN 17459:1992 X 8 NiCrAlTi 32 21 1.4959 SHT
≤ 50

170 500-750 35 L; 30 T
L: 120 J at RT
T: 80 J at RT
ASTM A 240/A 240M-03c 800H N08810 170
25
450
65
30
JIS G 3467:1988 NCF 800H TF S 175

450

30

t ≤ 0.187
310 45 690 100 30 100 HRB max
N08367 SA

t > 0.187
310
45
655
95
30 100 HRB max
ASTM A 249/A 249M-03
N08926 SA 295
43
650
94
35 100 HRB max

ASTM A 312/A 312M-03 N08926 HT 295
43
650
94
35

t ≤ 0.187
310 45 655 95 30
N08367 SA

t > 0.187
310
45
655
95
30 100 HRB max
ASTM A 688/A 688M-03
N08926 SA 295
43
650
94
35
O.D. < 10 27
10 ≤ O.D. < 20
30
JIS G 3463:1994 SUS836LTB ST
O.D. ≥ 20

205 520
35

Chapter 5 Steel Tubes and Pipes 246


Handbook of Comparative World Steel Standards
5.10 Line Pipe Steels

5.10.1A Mechanical Properties of Line Pipe Steels Without Notch Toughness Requirements

Thickness Yield Strength, min Tensile Strength, min
Standard
Designation
Grade, Class, Type,
Symbol or Name
Steel
Number
UNS
Number
Product Form/
Heat Treatment
t, mm t, in.
N/mm
2
or
MPa
ksi
N/mm

2
or
MPa
ksi
Elongation,
min, %
Other
A25 Class I - PSL 1
API 5L-2004
A25 CIass II - PSL 1
see standard 172 25 310 45 see standard
L175, Class I
ISO 3183-1:1996
L175, Class I
see standard 175 315 27
API 5L-2004 A - PSL 1 see standard 207 30 331 48 see standard
EN 10208-1:1997 L210GA 1.0319 see standard 210 335-475 25
ISO 3183-1:1996 L210 see standard 210 335 25
API 5L-2004 B - PSL 1 see standard 241 35 414 60 see standard
CSA Z245.1-2002 241 - Category I see standard 241-495 414-760 see standard
EN 10208-1:1997 L245GA 1.0459 see standard 245 415-555 22
ISO 3183-1:1996 L245 see standard 245 415 21
API 5L-2004 X42 - PSL 1 see standard 290 42 414 60 see standard
CSA Z245.1-2002 290 - Category I see standard 290-495 414-760 see standard
EN 10208-1:1997 L290GA 1.0483 see standard 290 415-555 21
ISO 3183-1:1996 L290 see standard 290 415 21
API 5L-2004 X46 - PSL 1 see standard 317 46 434 63 see standard
CSA Z245.1-2002 317 - Category I see standard 317 434 see standard
ISO 3183-1:1996 L320 see standard 320 435 20
API 5L-2004 X52 - PSL 1 see standard 359 52 455 66 see standard

CSA Z245.1-2002 359 - Category I see standard 359-530 455-760 see standard
EN 10208-1:1997 L360GA 1.0499 see standard 360 460-620 20
ISO 3183-1:1996 L360 see standard 360 460 19
API 5L-2004 X56 - PSL 1 see standard 386 56 490 71 see standard
CSA Z245.1-2002 386 - Category I see standard 386-540 490-760 see standard
ISO 3183-1:1996 L390 see standard 390 490 18
API 5L-2004 X60 - PSL 1 see standard 414 60 517 75 see standard
CSA Z245.1-2002 414 - Category I see standard 414-565 517-760 see standard
ISO 3183-1:1996 L415 see standard 415 520 17
API 5L-2004 X65 - PSL 1 see standard 448 65 531 77 see standard
CSA Z245.1-2002 448 - Category I see standard 448-600 531-760 see standard
ISO 3183-1:1996 L450 see standard 450 535 17
API 5L-2004 X70 - PSL 1 see standard 483 70 565 82 see standard
CSA Z245.1-2002 483 - Category I see standard 483-620 565-760 see standard
ISO 3183-1:1996 L485 see standard 485 570 16
CSA Z245.1-2002 550 - Category I see standard 550-690 620-830 see standard
ISO 3183-1:1996 L555 see standard 555 625-825 15
27 J at 0°C
see standard

Chapter 5 Steel Tubes and Pipes 247


Handbook of Comparative World Steel Standards
5.10 Line Pipe Steels

5.10.1B Chemical Composition of Line Pipe Steels Without Notch Toughness Requirements

Weight, %, max, Unless Otherwise Specified
Standard

Designation
Grade, Class, Type,
Symbol or Name
Steel
Number
UNS
Number
C Mn Si P S Cr Ni Mo Others
A25, Class I,
PSL 1 seamless
0.21 0.60 0.030 0.030
A25, Class II,
PSL 1 seamless
0.21 0.60 0.045-0.080 0.030
A25, Class I,
PSL 1 welded
0.21 0.60 0.030 0.030
API 5L-2004
A25, Class II,
PSL 1 welded
0.21 0.60 0.045-0.080 0.030
L175, Class I
S/NE/CE*
0.21 0.30-0.60 0.030 0.030 see standard
L175, Class II
S/NE/CE*
0.21 0.30-0.60 0.045-0.080 0.030 see standard
L175, Class I
W/EW/CW*
0.21 0.30-0.60 0.030 0.030 see standard

ISO 3183-1:1996
L175, Class II
W/EW/CW*
0.21 0.30-0.60 0.045-0.080 0.030 see standard
A, PSL 1 seamless 0.22 0.90 0.030 0.030
API 5L-2004
A, PSL 1 welded 0.22 0.90 0.030 0.030
EN 10208-1:1997 L210GA 1.0319 0.21 0.90 0.40 0.030 0.030 AL 0.015-0.060; Nb+V+Ti 0.15
L210 S/NE/CE* 0.22 0.90 0.030 0.030 see standard
ISO 3183-1:1996
L210 W/NE/CE* 0.21 0.90 0.030 0.030 see standard
B, PSL 1 seamless 0.28 1.20 0.030 0.030 Cb+V 0.03; Ti 0.04; Cb+V+Ti 0.15
API 5L-2004
B, PSL 1 welded 0.26 1.20 0.030 0.030 Cb+V 0.03; Ti 0.04; Cb+V+Ti 0.15
CSA Z245.1-2002 241 - Category I 0.26 2.00 0.50 0.030 0.035
Nb 0.11; Ti 0.11; V 0.11; B 0.001
CE 0.40 (see standard)
EN 10208-1:1997 L245GA 1.0459 0.20 1.15 0.40 0.030 0.030 AL 0.015-0.060; Nb+V+Ti 0.15
L245 S/NE/CE* 0.27 1.15 0.030 0.030 see standard
ISO 3183-1:1996
L245 W/NE/CE* 0.26 1.15 0.030 0.030 see standard
X 42, PSL 1 seamless 0.28 1.30 0.030 0.030 Ti 0.04; Cb+V+Ti 0.15
API 5L-2004
X 42, PSL 1 welded 0.26 1.30 0.030 0.030 Ti 0.04; Cb+V+Ti 0.15
CSA Z245.1-2002 290 - Category I 0.26 2.00 0.50 0.030 0.035
Nb 0.11; Ti 0.11; V 0.11; B 0.001
CE 0.40 (see standard)
EN 10208-1:1997 L290GA 1.0483 0.20 1.40 0.40 0.030 0.030 AL 0.015-0.060; Nb+V+Ti 0.15
L290 S/NE* 0.29 1.25 0.030 0.030 see standard
L290 S/CE* 0.29 1.25 0.030 0.030 see standard

ISO 3183-1:1996
L290 W/NE/CE* 0.28 1.25 0.030 0.030 see standard
*: See "Heat Treatment Terms" table at the beginning of the chapter.
Chapter 5 Steel Tubes and Pipes 248


Handbook of Comparative World Steel Standards
5.10 Line Pipe Steels

5.10.1B Chemical Composition of Line Pipe Steels Without Notch Toughness Requirements (Continued)

Weight, %, max, Unless Otherwise Specified
Standard
Designation
Grade, Class, Type,
Symbol or Name
Steel
Number
UNS
Number
C Mn Si P S Cr Ni Mo Others
X46, PSL 1 seamless 0.28 1.40 0.030 0.030 Ti 0.04; Cb+V+Ti 0.15
API 5L-2004
X46, PSL 1 welded 0.26 1.40 0.030 0.030 Ti 0.04; Cb+V+Ti 0.15
CSA Z245.1-2002 317 - Category I 0.26 2.00 0.50 0.030 0.035
Nb 0.11; Ti 0.11; V 0.11; B 0.001
CE 0.40 (see standard)
L320, S/NE* 0.31 1.35 0.030 0.030 see standard
L320 S/CE* 0.29 1.25 0.030 0.030 see standard
L320 W/NE* 0.30 1.25 0.030 0.030 see standard

ISO 3183-1:1996
L320 W/CE* 0.28 1.25 0.030 0.030 see standard
X52, PSL 1 seamless 0.28 1.40 0.030 0.030 Ti 0.04; Cb+V+Ti 0.15
API 5L-2004
X52, PSL 1 welded 0.26 1.40 0.030 0.030 Ti 0.04; Cb+V+Ti 0.15
CSA Z245.1-2002 359 - Category I 0.26 2.00 0.50 0.030 0.035
Nb 0.11; Ti 0.11; V 0.11; B 0.001
CE 0.40 (see standard)
EN 10208-1:1997 L360GA 1.0499 0.22 1.45 0.55 0.030 0.030 AL 0.015-0.060; Nb+V+Ti 0.15
L 360 S/NE* 0.31 1.35 0.030 0.030 see standard
L360 S/CE* 0.29 1.25 0.030 0.030 see standard
L360 W/NE* 0.30 1.25 0.030 0.030 see standard
ISO 3183-1:1996
L360 W/CE* 0.28 1.25 0.030 0.030 see standard
X56, PSL 1 seamless 0.28 1.40 0.030 0.030 Ti 0.04; Cb+V+Ti 0.15
API 5L-2004
X56, PSL 1 welded 0.26 1.40 0.030 0.030 Ti 0.04; Cb+V+Ti 0.15
CSA Z245.1-2002 386 - Category I 0.26 2.00 0.50 0.030 0.035
Nb 0.11; Ti 0.11; V 0.11; B 0.001
CE 0.40 (see standard)
L390, S/NE/CE* 0.26 1.35 0.030 0.030 see standard
ISO 3183-1:1996
L390, W/NE/CE* 0.26 1.35 0.030 0.030 see standard
X60, PSL 1 seamless 0.28 1.40 0.030 0.030 Ti 0.04; Cb+V+Ti 0.15
API 5L-2004
X60, PSL 1 welded 0.26 1.40 0.030 0.030 Ti 0.04; Cb+V+Ti 0.15
CSA Z245.1-2002 414 - Category I 0.26 2.00 0.50 0.030 0.035
Nb 0.11; Ti 0.11; V 0.11; B 0.001
CE 0.40 (see standard)
L415 S/NE/CE* 0.26 1.35 0.030 0.030 see standard

ISO 3183-1:1996
L415 W/NE/CE* 0.26 1.35 0.030 0.030 see standard
X65, PSL 1 seamless 0.28 1.40 0.030 0.030 Ti 0.06; Cb+V+Ti 0.15
API 5L-2004
X65, PSL 1 welded 0.26 1.45 0.030 0.030 Ti 0.06; Cb+V+Ti 0.15
CSA Z245.1-2002 448 - Category I 0.26 2.00 0.50 0.030 0.035
Nb 0.11; Ti 0.11; V 0.11; B 0.001
CE 0.40 (see standard)
L450 S/NE/CE* by agreement
ISO 3183-1:1996
L450 W/NE/CE* 0.26 1.40 0.030 0.030 see standard
*: See "Heat Treatment Terms" table at the beginning of the chapter.
Chapter 5 Steel Tubes and Pipes 249


Handbook of Comparative World Steel Standards
5.10 Line Pipe Steels

5.10.1B Chemical Composition of Line Pipe Steels Without Notch Toughness Requirements (Continued)

Weight, %, max, Unless Otherwise Specified
Standard
Designation
Grade, Class, Type,
Symbol or Name
Steel
Number
UNS
Number
C Mn Si P S Cr Ni Mo Others

X70, PSL 1 seamless 0.28 1.40 0.030 0.030 Ti 0.04; Cb+V+Ti 0.15
API 5L-2004
X70, PSL 1 welded 0.26 1.65 0.030 0.030 Ti 0.04; Cb+V+Ti 0.15
CSA Z245.1-2002 483 - Category I 0.26 2.00 0.50 0.030 0.035
Nb 0.11; Ti 0.11; V 0.11; B 0.001
CE 0.40 (see standard)
L485, S/NE/CE* by agreement
ISO 3183-1:1996
L485 W/NE/CE* 0.23 1.60 0.030 0.030 see standard
CSA Z245.1-2002 550 - Category I 0.26 2.00 0.50 0.030 0.035
Nb 0.11; Ti 0.11; V 0.11; B 0.001
CE 0.40 (see standard)
L555 S/NE/CE* by agreement
ISO 3183-1:1996
L555 W/NE/CE* 0.18 1.80 0.030 0.030 see standard
*: See "Heat Treatment Terms" table at the beginning of the chapter.

Chapter 5 Steel Tubes and Pipes 250


Handbook of Comparative World Steel Standards
5.10 Line Pipe Steels

5.10.2A Mechanical Properties of Line Pipe Steels With Notch Toughness Requirements

Thickness Yield Strength, min Tensile Strength, min
Standard
Designation
Grade, Class, Type,
Symbol or Name

Steel
Number
UNS
Number
Product Form/
Heat Treatment
t, mm t, in.
N/mm
2
or
MPa
ksi
N/mm
2
or
MPa
ksi
Elongation,
min, %
Other
ASTM A 1005/A 1005M-00 35 240-450 35-65 415 60 see standard see standard
API 5L-2004 B - PSL 2 see standard 241-448 35-65 414-758 60-110 see standard
L: 41 J at 0°C; T: 27 J at 0°C
see standard
CSA Z245.1-2002 241 - Category II or III see standard 241-495 414-760 see standard
OD < 457 mm: 27 J at temp
OD ≥ 457 mm: 40 J at temp
see standard

NPS < 8

240 35
ASTM A 984/A 984M-03 35 see standard

NPS ≤ 8
240-450 35-65
415 60 see standard see standard
L245NB 1.0457
EN 10208-2:1996
L245MB 1.0418
see standard 245-440 415 22 see standard
L245NB
ISO 3183-2:1996
L245MB
see standard 245-440 415 22 see standard
API 5L-2004 X42 - PSL 2 see standard 290-496 42-72 414-758 60-110 see standard
L: 41 J at 0°C; T: 27J at 0°C
see standard
CSA Z245.1-2002 290 - Category II or III see standard 290-495 414-760 see standard
OD < 457 mm: 27 J at temp
OD ≥ 457 mm: 40 J at temp
see standard
L290NB 1.0484
EN 10208-2:1996
L290MB 1.0429
see standard 290-440 415 21 see standard
L290NB
ISO 3183-2:1996
L290MB
see standard 290-440 415 21 see standard
API 5L-2004 X46 - PSL 2 see standard 317-524 46-76 434-758 63-110 see standard

L: 41 J at 0°C; T: 27J at 0°C
see standard;
CSA Z245.1-2002 317 - Category II or III see standard 317 434 see standard
OD < 457 mm: 27 J at temp
OD ≥ 457 mm: 40 J at temp
see standard

Chapter 5 Steel Tubes and Pipes 251


Handbook of Comparative World Steel Standards
5.10 Line Pipe Steels

5.10.2A Mechanical Properties of Line Pipe Steels With Notch Toughness Requirements (Continued)

Thickness Yield Strength, min Tensile Strength, min
Standard
Designation
Grade, Class, Type,
Symbol or Name
Steel
Number
UNS
Number
Product Form/
Heat Treatment
t, mm t, in.
N/mm
2
or

MPa
ksi
N/mm
2
or
MPa
ksi
Elongation,
min, %
Other
API 5L-2004 X52 - PSL 2 see standard 359-531 52-77 455-758 66-110 see standard
L: 41 J at 0°C; T: 27J at 0°C
see standard
CSA Z245.1-2002 359 - Category II or III see standard 359-530 455-760 see standard
OD < 457 mm: 27 J at temp
OD ≥ 457 mm: 40 J at temp
see standard
L360NB 1.0582
L360QB 1.8948
EN 10208-2:1996
L360MB 1.0578
see standard 360-510 460 20 see standard
L360NB
L360QB
ISO 3183-2:1996
L360MB
see standard 360-510 460 20 see standard

NPS < 8
345 50

ASTM A 984/A 984M-03 50 see standard

NPS ≤ 8
345-530 50-77
485 70 see standard see standard
API 5L-2004 X56 - PSL 2 see standard 386-544 56-79 490-758 71-110 see standard
L: 41 J at 0°C; T: 27J at 0°C
see standard
CSA Z245.1-2002 386 - Category II or III see standard 386-540 490-760 see standard
OD < 457 mm: 27 J at temp
OD ≥ 457 mm: 40 J at temp
see standard
API 5L-2004 X60 - PSL 2 see standard 414-565 60-82 517-758 75-110 see standard
L: 41 J at 0°C; T: 27J at 0°C
see standard
CSA Z245.1-2002 414 - Category II or III see standard 414-565 517-760 see standard
OD < 457 mm: 27 J at temp
OD ≥ 457 mm: 40 J at temp
see standard
ASTM A 1005/A 1005M-00 60 415-550 60-80 515 75 see standard see standard
L415NB 1.8972
L415QB 1.8947
EN 10208-2:1996
L415MB 1.8973
see standard 415-565 520 18 see standard
L415NB
L415QB
ISO 3183-2:1996
L415MB
see standard 415-565 520 18 see standard